外墻膩子粉裂紋裂縫的產生主要來自“內因”和“外因”兩個方面，“內因”方面解決辦法主要集中在產品的生產和原材料的技術性能上，“外因”方面相對要復雜些，涉及到建筑結構設計、施工工藝與技術水平、工程質量監督與管理、自然環境狀況等多方面。

The occurrence of cracks in exterior wall putty powder mainly comes from two aspects: "internal factors" and "external factors". The solutions for "internal factors" mainly focus on the production of products and the technical performance of raw materials, while the "external factors" are relatively more complex, involving various aspects such as building structure design, construction technology and technical level, engineering quality supervision and management, and natural environmental conditions.

一、聚合物抹面砂漿、水泥類膩子的防裂性，核心在原材料的選擇上，選用優良的原材料、充分認識和了解各種原輔材料性質與作用機理，科學配方，選用功能性強的、性能穩定可靠的優良產品，能較好地預防裂縫的產生。

1、 The crack resistance of polymer plastering mortar and cement putty focuses on the selection of raw materials. High quality raw materials are selected, and the properties and mechanisms of various raw and auxiliary materials are fully understood. Scientific formulas are used, and high-quality products with strong functionality, stable and reliable performance are selected to effectively prevent the occurrence of cracks.

二、建筑設計非常是外墻保溫構造設計上應嚴謹，應充分考慮地基沉降、抗震、抗風壓、應力釋放、環境影響等問題。

2、 Architectural design, especially the exterior wall insulation structure design, should be rigorous and fully consider issues such as foundation settlement, earthquake resistance, wind pressure resistance, stress release, and environmental impact.

三、施工工藝上，為避免抹面砂漿、外墻膩子產生較大的干縮力，每次刮抹均應宜薄不宜厚，抹面砂漿每次刮抹不超過2.5MM層厚，外墻膩子每次刮抹不超過1MM層厚。

3、 In terms of construction technology, in order to avoid significant drying shrinkage caused by plastering mortar and exterior wall putty, each scraping should be thin rather than thick. The plastering mortar should not exceed a layer thickness of 2.5mm each time, and the exterior wall putty should not exceed a layer thickness of 1mm each time.

四、外墻保溫層的設計與施工均未考慮到保溫層內應力的釋放問題，整個墻面從上至下幾層、幾十層樓高一氣呵成，沒有設計伸縮縫，一旦產生較大的應力，整個保溫層乃抹面砂漿、外墻膩子、涂料層就會不可避免產生裂縫。

4、 The design and construction of the external wall insulation layer did not take into account the issue of stress release inside the insulation layer. The entire wall is several floors from top to bottom, dozens of floors high, and there are no expansion joints designed. Once significant stress is generated, cracks will inevitably occur in the entire insulation layer, including the plastering mortar, external wall putty, and coating layer.

五、干混抹面砂漿、外墻膩子或常用水泥中不宜過量、過多使用聚乙烯醇類、乳膠類等封閉性良好的膠粘劑，此類膠粘劑能迅速成膜和封閉水泥微孔，并加劇水泥產生干縮力，形成“硬殼”現象，與基層形成較大的強度差，即面層強度大大超過基層強度，容易造成龜裂、空鼓、脫落。此外，水泥砂漿微孔一旦被完全封閉，這不僅會影響水泥充分水化、而且會使水泥砂漿喪失“自由呼吸”和自養護功能，墻體中不良成份不能隨水份通過微細孔淅出，墻體使用壽命就會較差。

5、 Excessive use of strong sealing adhesives such as polyvinyl alcohol and latex should not be used in dry mix mortar, exterior wall putty, or commonly used cement. These adhesives can quickly form a film and seal cement micropores, exacerbate the drying shrinkage force of cement, form a "hard shell" phenomenon, and form a significant strength difference with the base layer. That is, the strength of the surface layer greatly exceeds the strength of the base layer, which is prone to cracking, hollowing, and peeling. In addition, once the micropores of cement mortar are completely sealed, it will not only affect the full hydration of cement, but also cause the cement mortar to lose its "free breathing" and self curing function. Poor components in the wall cannot be separated with water through the micro pores, and the service life of the wall will be poor.

本文由濟南石膏粉友情奉獻.更多有關的知識請點擊:http://m.gyxxhyy120.com真誠的態度.為您提供為多維度的服務.更多有關的知識我們將會陸續向大家奉獻.敬請期待.

This article is dedicated by Jinan gypsum powder. For more information, please click: http://m.gyxxhyy120.com Sincere attitude. We will provide you with comprehensive service. We will gradually contribute more relevant knowledge to everyone. Stay tuned